Refining processes of selected copper alloys
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 2
Abstract
The analysis of the refining effectiveness of the liquid copper and selected copper alloys by various micro additions and special refining substances – was performed. Examinations of an influence of purifying, modifying and deoxidation operations performed in a metal bath on the properties of certain selected alloys based on copper matrix - were made. Refining substances, protecting-purifying slag, deoxidation and modifying substances containing micro additions of such elements as: zirconium, boron, phosphor, sodium, lithium, or their compounds introduced in order to change micro structures and properties of alloys, were applied in examinations. A special attention was directed to macro and micro structures of alloys, their tensile and elongation strength and hot-cracks sensitivity. Refining effects were estimated by comparing the effectiveness of micro structure changes with property changes of copper and its selected alloys from the group of tin bronzes.
Authors and Affiliations
S. Rzadkosz, M. Kranz, P. Nowicki
Keywords
Related Articles
- EP ID EP71700
- DOI -
- Views 79
- Downloads 0
Effect of overheating degree on the solidification parameters of AlSi17CuNiMg silumin
Melting technology, especially the temperature of overheating and pouring above the liquidus point Tliq as well as the cooling rate, determine alloy macro - and microstructure, and hence also casting performance proper...
Initial assessment of effectiveness of some selected inoculants for grey cast iron
The influence of four inoculants: FeSi75, Zircinoc, Foundry Grade, and Inogen has been determined in the work. The additions have been introduced in the amount of 0,2% into the cast iron exibiting the degree of saturatio...
Registration of melting and crystallization process of MCMgLi8Ca5 alloy with use of ATND method
Among lightweight metal alloys, magnesium is the lightest structural material with density of 1.74 g/cm3, having many attractive physical and mechanical properties combined with processing advantages. Therefore, it repre...
Influence analysis foamed polystyrene model on casting defects as well as microstructure ductile cast iron from Lost Foam process with Inmold method
In this work was shown a influence analysis foamed polystyrene model on casting defects as well as microstructure ductile cast iron from Lost Foam process with Inmold method.
The influence of ceramic fibre on thermal expansion of moulding materials for investment casting technology
The results of dilatometric measurements presented in the paper are a supplement to the investigations concerning broadening the composition of ceramic slurry intended for investment casting technology with ceramic fibre...