The analysis of carbon attendance in copper alloys as reason of gas porosity
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 3
Abstract
In the work show, that opinions the leaning on it dissolubilities of carbon can be recognized (and only in approximation) only for copper about large purity. They do not concern it her mostly multiple alloys, at which the majority of alloy additions marks with possibility of creating carbides. Equally important the possibility of creating of carbides of accidental dirts is. Introduced and investigation own arguments authorize to conclusion that the technological process of fusion of copper alloys does not it be to characterize in relation with separate guilds to different alloys and should to be to hold on valid in steel - makes principles.
Authors and Affiliations
A. W. Bydałek
Keywords
Related Articles
- EP ID EP71987
- DOI -
- Views 80
- Downloads 0
Application of microjet in heat treatment of aluminium bronzes
Mechanical properties of a CuAl10Fe4Ni4 bronze subjected to solution heat treatment and toughening were examined. In solution heat treatment, a microjet was used to raise the cooling rate. A slight increase of mechanical...
Ultrasonic testing of the hardening kinetics of epoxy resins used for foundry patterns
The study presents the results of investigations on the hardening kinetics of modern pattern materials which, among others, include also epoxy resins. Tests were carried out using a new ultrasonic technique developed by...
Control of cast iron and casts manufacturing by Inmold method
In this paper the usability of cast iron spheroidizing process in mould control by ATD method as well as by ultrasonic method were presented. Structure of instrumentation needed for control form performance of cast iron...
Fractographic research of the C45 steel remelted with a plasma of electric arc
This work presents research into properties of the surface layer of the C45 steel following the treatment with highly-focused thermal stream utilizing the GTAW method. The remelting of the surface layer of the sample was...
Laboratory grey cast iron continuous casting line with electromagnetic forced convection support
The article describes the construction of a 20 mm diameter grey cast iron ingots continuous casting laboratory line. This line is made of three main units: melting unit (induction furnace), casting unit and the pulling u...