The comparative studies of ADI versus Hadfield cast steel wear resistance
Journal Title: Archiwum Odlewnictwa - Year 2011, Vol 11, Issue 2
Abstract
The results of comparative studies of wear resistance of ADI versus high manganese Hadfield cast steel are presented. For evaluation of wear resistance three type of ADI were chosen. Two of them were of moderate strength ADI with 800 and 1000MPa tensile strength while the third was 1400MPa tensile strength ADI. The specimens were cut from ADI test YII type casting poured and heat treated in Institute of Foundry in Krakow. The pin on disc method was used for wear resistance experiment. The specimens had a shape of 40mm long rod with diameter 6mm. The load and speed were 100N and 0,54m/s respectively. It was concluded that the wear resistance of ADI is comparable with high manganese cast steel and in case of low tensile grade ADI and is even better for high strength ADI than Hadfield steel.
Authors and Affiliations
P. Skoczylas, A. Krzyńska, M. Kaczorowski
Keywords
Related Articles
- EP ID EP72527
- DOI -
- Views 97
- Downloads 0
The Dependence of Castings Quality Produced in Clay Moulding Mixtures from the Properties of Binder Based on a Montmorillonite
Casting quality depends on many factors including the quality of the input materials, technology, material securing and last but not least, the mould into which the casting is casted. By pouring into a single-shot mould,...
The influence of microstructure on the mechanical properties of metallurgical rolls made of G200CrMoNi4-3-3 cast steel
The subject of the study is the high-carbon tool cast steel G200CrMoNi4-3-3 used for metallurgical rolls, especially in section rolling mills. The test material was derived from a roll damaged in production; therefore, t...
Corrosion behaviour of the AlSi6Cu4 alloy and cast AlSi6Cu4-graphite particles composite
The corrosion behaviour of the AlSi6Cu4 alloy as a composite matrix and of composites with 8% vol. of graphite particles was investigated. The corrosion experiments were performed over a range of elevated temperatures an...
Influence of a matrix on properties of mottled cast iron applied for mill rolls
Mill rolls are ones of the most expensive tools applied in plastic working processes and have to satisfy several criteria, which allow them to be used. Cast iron mill rolls, due to their fracture toughness and tribologic...
Effect of Magnesium Oxide Nanoparticles on Water Glass Structure
An attempt has been made to determine the effect of an addition of colloidal suspensions of the nanoparticles of magnesium oxide on the structure of water glass, which is a binder for moulding and core sands. Nanoparticl...