THE INFLUENCE OF THE STRUCTURE OF ETHOXYLATED FATTY ALCOHOL ALKYL CHAIN ON TRIBOLOGICAL PROPERTIES OF THEIR AQUEOUS SOLUTIONS
Journal Title: Tribologia - Year 2011, Vol 235, Issue 1
Abstract
The influence of the structure of ethoxylated fatty alcohol alkyl chain on physical-chemical and tribological properties of their aqueous solutions is analysed in the paper. Aqueous solutions of mixtures of two alcohols, containing 12 and 14 carbon atoms in alkyl chains, ethoxylated with 7 and 10 moles of ethylene oxide (iso-C13EO7 and iso-C13EO9) were tested. Surface activity was measured as surface tension and the angle of wetting steel. Tribological characteristics were expressed in terms of motion resistance and wear under constant load. A ball-on-disc tribometer (T-11 tester) was employed. It was observed that isoalcohols revealed a better ability to reduce surface tension and worse to wet steel surfaces, as compared to alcohols containing linear alkyl chains in their structures. It was proved that, under small loads (10.5 N), the reduction of motion resistance and wear was significantly smaller in the case of alcohols containing branched chains than in the case of their linear analogues. The changes of the tribological properties observed could be interpreted in terms of the lower durability of the lubricating film formed by the isoalcohols from their solutions. The film created under conditions of friction is not durable and does not protect the cooperating elements of the friction couple against wear. That is why the aqueous solutions of isoalcohols cannot be used as efficient lubricants.<br/><br/>
Authors and Affiliations
Marian W. Sułek, Tomasz Wasilewski, Anita Bocho-Janiszewska, Anna Małysa
Keywords
Related Articles
- EP ID EP271843
- DOI -
- Views 40
- Downloads 0
OCENA ODPORNOŚCI NA ZUŻYCIE I KOROZJĘ ZŁĄCZY WYKONANYCH POMIĘDZY TYTANEM A STALĄ NIERDZEWNĄ ZA POŚREDNICTWEM Al, Cu ORAZ Ni
W niniejszej pracy połączono czysty tytan (Grade 2) ze stalą nierdzewną (X5CrNi18-10) poprzez spajanie dyfuzyjne z użyciem międzywarstw z aluminium, miedzi oraz niklu (100 μm). Badanie koncentruje się na porównaniu odpor...
SURFACE RANDOM PARAMETERS FOR ENDOPROSTHESIS LUBRICATION
Within the last ten years in the European Union the number of bone fractures caused by the osteoarthritis increased twofold. More than 100000 hip or knee joints in total have been implanted in Germany during one year. Wi...
Właściwości tribolgiczne warstwy wierzchniej z borem w warunkach tarcia ślizgowego
Właściwości tribologiczne par ciernych zależą od ich konstrukcji, zastosowanych materiałów i przeprowadzonej obróbki powierzchniowej elementów pary. Celem badań było wyznaczenie wpływu modyfikacji warstwy powierzchniowej...
METODYCZNE ASPEKTY WYZNACZANIA KINETYCZNEGO WSPÓŁCZYNNIKA TARCIA ZIARNIAKÓW PSZENICY METODĄ RÓWNI POCHYŁEJ
Jednym z bardziej popularnych sposobów wyznaczania tzw. kinetycznego współczynnika tarcia zewnętrznego między parą ciał stałych jest metoda równi pochyłej. Niestety, manualny pomiar czasu ruchu cząstki (zazwyczaj za pomo...
TRIBOLOGICAL PROPERTIES OF A FRICTION PAIR WITH KINDS OF BRONZES
This paper presents the results of tribological properties with of a friction pair steel X210Cr12 (60 HRC) and bronze CuSn12Ni2 (in the form of casting and sintered) and engine trade lubricated oil Selektol Special SD 20...