THE TRIBOLOGICAL PROPERTIES OF FERROUS BASED COATINGS FORMED USING DIFFERENT TECHNOLOGICAL METHODS
Journal Title: Tribologia - Year 2011, Vol 237, Issue 3
Abstract
Plasma-sprayed coatings on the base self-fluxing alloys were investigated. Clean ferrous-based alloy P-Cr16Fe5B4Si4 was used as well as the same with the addition of TaB, MoB, and B4C powders. Fire and laser washing were used to form coatings. The thickness measurements of coatings after processing were from 0.5–0.7 mm, on the base material of steel C45. The metallographic analysis indicated that coating structure depends on the chemical composition of the powder as well as the coating technology. When using an Amsler friction-wear machine, it was determined that when dry technical friction increasingly spreads of torque of friction are observed after some minutes of work, and when oil friction torque are very stable. Additional MoB laser alloying of the coating on a base of P-Cr4Mn2B4Si2V1 powder guarantees a minimal value of the mean friction coefficient. However, the minimal value of the momentary friction coefficient was registered for the coating with additional B4C laser alloying. During dry technical friction, using a coating on a base of P-Cr4Mn2B4Si2V1 powder with additional MoB or B4C laser alloying guarantees a multiple decrease in wear intensity. The presence of oil decreases the influence of material and technology of coating on wear intensity, the difference of values is no more then 20%.<br/><br/>
Authors and Affiliations
Eugene Feldshtein, Margarita A. Kardapolova
Keywords
Related Articles
- EP ID EP271516
- DOI -
- Views 55
- Downloads 0
ANALIZA WŁAŚCIWOŚCI TRIBOLOGICZNYCH NANOKOMPOZYTOWEJ POWŁOKI TiN/Si3N4 W STYKU ŚLIZGOWYM Z PRZECIWELEMENTEM CERAMICZNYM, STALOWYM I POLIMEROWYM
W niniejszej pracy dokonano analizy tarcia i zużycia twardej powłoki nanokompozytowej TiN/Si3N4 podczas współpracy z kulami ceramicznymi Al2O3, stalowymi 100Cr6 i polimerowymi PTFE. Powłoka została osadzona na próbkach z...
BADANIE PROCESÓW ZUŻYCIOWYCH PŁYNU HAMULCOWEGO W ZŁOŻONYCH WARUNKACH WYMUSZEŃ
W pracy określono wpływ zwiększonej zawartości wody w płynie hamulcowym poprzez pomiar jego zawodnienia i temperatury wrzenia oraz badanie wpływu zużycia płynu hamulcowego na bezpieczeństwo i niezawodność układu hamulcow...
TRIBOLOGICAL PROPERTIES OF Al2O3 + TiO2 COATINGS MANUFACTURED BY PLASMA SPRAYING
In the paper the results of tribological, microscopic, and mechanical research of Al2O3 + TiO2 coatings manufactured by plasma spraying are presented. The feeding material was a powder Al2O3 + 13 wt.% TiO2 (Metco 6221, O...
FRICTION PROCESSES OF SELECTED POLYMERS SLIDING ON STEEL AND DURALUMIN IN A LUBRICANT ENVIRONMENT
The article presents the results of tribological research into engineering polymers (POM, PEEK, PPS) cooperating in sliding motion with 316L steel and EN AW-2017A aluminium alloy in the presence of a liquid (water, hydra...
PORÓWNANIE ODPORNOŚCI NA ZUŻYWANIE ŚCIERNE STALI HARDOX 500 i 20MnCr5
W pracy przedstawiono wyniki badań eksperymentalnych dotyczących odporności na zużywanie ścierne stali Hardox 500 i stali 20MnCr5 poddanej obróbce cieplno-chemicznej. Stale te często stosuje się na elementy maszyn rolnic...