TRIBOTECHNICAL CHARACTERISTICS OF POWDER MATERIALS BASED ON IRON AFTER BORIDING
Journal Title: Проблеми тертя та зношування - Year 2017, Vol 76, Issue
Abstract
The structure, phase composition of the boride coating deposited on the powder material SP90- D3 is studied. It is shown that borating substantially increases the wear resistance of the powder material.
Authors and Affiliations
V. F. LABUNETS, M. I. DENІSENKO, G. G. GOLEMBIYEVSKYY
Keywords
Related Articles
- EP ID EP366349
- DOI -
- Views 48
- Downloads 0
ANALYTICAL EVALUATION OF LIMIT VALUES OF FRICTION FACTOR DURING BURNISHING WITH METAL-CONTAINIING LUBRICANT
The theoretical research of the interaction the surface with deforming tool parts at burnishing with metal-containing lubricant, which is effective for the treatment of parts made of titanium alloys, is described in the...
Professor M. Pashechko creative career
Professor M. Pashechko creative career
ESTIMATION OF HEAT PROCESSES IN THE FRICTION CONTACT UNDER ROLLING WITH SLIPPAGE CONDITION
The influence of slip velocity at rolling with slippage on the intensity of heat release in the local contact at different modes of lubricating action was examined. Method of estimation of tem-perature resistance of the...
RESEARCH OF TRIBOTECHNICAL CHARACTERISTICS OF HIGH-SPEED STEEL Р6М5 WITH THE COMBINED COATING
The influence of integrated laser treatment and ion-plasma coating on the tribotechnical char-acteristics of high-speed steel R6M5 under conditions of slip friction without lubrication and abrasive wear has been establis...
MODERN FUNCTIONAL MATERIALS FROM NANOSTRUCTURED BAINITE MATRIX AND INCREASED TRIBOLOGIE PROPERTIES
Conformities to law of forming of nanostructure matrix was investigate in wearproof high-chromium cast-irons, mechanical, physical and chemical, tribology properties are conditioned the presence of elements of nanostruct...