White and gray solidification of the Fe-C eutectic
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 3
Abstract
The mechanism of structure transition from stable to metastable eutectic is the object of the publication. The influence of micro-segregation elements on forming different phase, growth undercooling and growth rates was determined. Also competitive growth of both eutectic in alloys Fe-C was introduced.
Authors and Affiliations
M Trepczyńska-Łent
Keywords
Related Articles
- EP ID EP72038
- DOI -
- Views 109
- Downloads 0
Nitrogen hardening of creep-resistant G-NiCr28W alloy
In the group of creep-resistant materials, most important are heat-resistant nickel-based alloys. The G-NiCr28W alloy subject to detailed examinations was observed to have two different austenite-like phases. In the inte...
Basics of control system material in iron foundry
The article is taking into account problems of preparing the production of cast-iron casts with reference to correctnesses functioning of processes supplementing, containing elements the system of supply necessary materi...
Tribological properties of AC44200 based composites strenghead with AlB2BOB3 Bparticles
The paper presents a research on abrasion resistance of aluminium-based composites consisting of EN AC-44200 matrix reinforced with AlB2BOB3B particles. The examinations revealed that wear intensity of the composites dec...
Registration of melting and crystallization process of MCMgLi8Ca5 alloy with use of ATND method
Among lightweight metal alloys, magnesium is the lightest structural material with density of 1.74 g/cm3, having many attractive physical and mechanical properties combined with processing advantages. Therefore, it repre...
Plasticity of the AlSi9Mg alloy modified with Na, F and Cl compounds
This paper presents the results of an experiment investigating the structure and the percent elongation of an AlSi9Mg alloy modified with NaCl, Na3AlF6 and NaF compounds. The alloy was modified in a crucible. The experim...