Comparison of Mechanical Properties Between three Different Types of T-loop
Journal Title: Journal of Dental Biomaterials - Year 2015, Vol 2, Issue 2
Abstract
Statement of Problem: T-loop is one of the most popular closing loops in orthodontic profession. However its activation is in the contrary to Bouschinger effect theory, since the formed bends would be opened during activation. The purpose of this study was to add a helix in a way to be more respondent to the Bouschinger effect theory. Objectives: To compare the load deflection, maximal elastic load and range between three different types of T-loop. Materials and Methods: 5 sample of each 3 different designs of T-loop (group 1: original T-loop, group 2: T-loop with the two inner helices, group 3: T-loop with the two helices constructed outside the horizontal part) had been tested with universal testing machine (Instron). The load –deflection curves was plotted and the mechanical properties (load deflection, maximal elastic load and range) were measured. One way ANOVA was used to identify statistical differences between designs. Results: The mean value of maximal elastic load in group 1 (6.02±0.27) was significantly higher than group 2 (5.16±0.46) and in group 2 were significantly higher than group3 (4.35±0.25) (p<0.001). A significantly higher load deflection was reported in group 1 (0.73±0.36) in comparison to group2 (0.56±0.74) and group 3(0.56±0.69) (p=0.002), with no significant difference between two latest groups (p=0.999). The mean range in group 3 (4.15±0.10) was significantly lower than group 1(5.43±0.13) and group 2 (5.59±0.15) (p=<0.001) with no significant difference between group 1 and 2 (p=0.149). Conclusions: The results revealed that increasing length of T-loop with helices will decrease Load deflection rate the place and design of helices might not be a crucial factor. The new design of T-loop with helices relevant to Bouschinger effect theory needs a further survey regarding their position.
Authors and Affiliations
Sh Ajami, M Oshagh, F Torabinejad, Z Behroozi
Keywords
Related Articles
- EP ID EP248910
- DOI -
- Views 110
- Downloads 0
Chemical Stability of Bioglass in Simulated Oral Environment
Statement of Problem: Bioglasses are a series of biocompatible dental materials, which are considered as light conducting inserts in resin composite restorations. Consequently, their chemical stability is more essential...
Comparative Study of Shear Bond Strength of Three Veneering Ceramics to a Zirconia Core
Statement of Problem: Fracture of veneering porcelain has been described as the most frequent reason for the failure of zirconia-based fixed restorations. Objectives: The purpose of this study was to evaluate and compare...
Antimicrobial Effect of Copper Oxide Nanoparticles on Some Oral Bacteria and Candida Species
ABSTRACT Statement of Problem: Acid producing bacteria including Streptococcus mutans and lactobacilli cause tooth demineralization and lead to tooth decay. Also, oral colonization of the species of Candida has been repo...
Fracture Toughness Evaluation of Hybrid and Nano-hybrid Resin Composites after Ageing under Acidic Environment
Statement of Problem: Tooth-coloured restorative materials are brittle with the major shortcomings of sensitivity to flaws and defects. Although various mechanical properties of resin composites have been studied, no fra...
The Effect of Time Intervals on Heat Transfer to the Implant-Bone Interface during Preparation of a Titanium Abutment: An in Vitro Study
Statement of Problem: Thermal injury during dental implant placement and restoration is a clinical concern as it may cause bone damage and compromise osseointegration. The threshold level for heat-induced cortical bone n...