Energy dissipation mechanism and damage model of marble failure under two stress paths
Journal Title: Frattura ed Integrità Strutturale - Year 2014, Vol 8, Issue 30
Abstract
Marble conventional triaxial loading and unloading failure testing research is carried out to analyze the elastic strain energy and dissipated strain energy evolutionary characteristics of the marble deformation process. The study results show that the change rates of dissipated strain energy are essentially the same in compaction and elastic stages, while the change rate of dissipated strain energy in the plastic segment shows a linear increase, so that the maximum sharp point of the change rate of dissipated strain energy is the failure point. The change rate of dissipated strain energy will increase during unloading confining pressure, and a small sharp point of change rate of dissipated strain energy also appears at the unloading point. The damage variable is defined to analyze the change law of failure variable over strain. In the loading test, the damage variable growth rate is first rapid then slow as a gradual process, while in the unloading test, a sudden increase appears in the damage variable before reaching the rock peak strength. According to the deterioration law of damage and the impact of confining pressure on the elastic modulus, a rock damage constitutive model is established, which has a better fitting effect on the data in the loading and unloading failure processes.
Authors and Affiliations
Liming Zhang, Minyuan Ren, Shaoqiong Ma, Zaiquan Wang
Keywords
Related Articles
- EP ID EP88939
- DOI -
- Views 52
- Downloads 0
Effect of molding processes on multiaxial fatigue strength in short fibre reinforced polymer
This study concerns the multiaxial static and fatigue strength properties. Short-glass-fibre-reinforced phenolic-resin composites (SGP) molded by injection and compression processes were subjected to tensiontorsio...
Variation of Stress intensity factor and elastic T-stress along the crack-front in finite thickness plates
Non-singular terms in the series expansion of the elastic crack-tip stress fields, commonly referred to as the T-stress. The T-stress is as an additional stress field characterizing parameter to stress intensity factor (...
Are the Paris’ law parameters dependent on each other?
The question about the existence of a correlation between the parameters C and m of the Paris’ law is re-examined in this paper. According to dimensional analysis and incomplete self-similarity concepts applied to...
Crack path dependence on inhomogeneities of material microstructure
Crack trajectories under different loading conditions and material microstructural features play an important role when the conditions of crack initiation and crack growth under fatigue loading have to be evaluated...
Integrated structure for a resonant micro-gyroscope andaccelerometer
This paper presents the study of the mechanical behavior of a microstructure designed to detectacceleration and angular velocity simultaneously. The new resonant micro-sensor proposed, fabricated by theThELMA© surf...